The effect of the process temperature on the bondability in diffusion bonding of AISI 430 with nodular cast iron
[ X ]
Tarih
2006
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Carl Hanser Verlag
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
The effect of process temperature on the bondability of stainless steel AISI 430 and nodular cast iron was studied. The diffusion bonding was investigated experimentally under a protective atmosphere at various temperatures and a prescribed constant pressure blow which would cause macro-deformation. Microstructure examinations were carried out with the help of optical microscopy, SEM and EDS. Hardness values were measured by HV scale under a load of 200 g. At the bond interface cross section, decarburized and dechromised regions were observed on the ductile cast iron side and the stainless steel side respectively. Best mechanical and metallurgical properties were observed for the specimen bonded at 1100 degrees C process temperature at 15 MPa, for 20 min. As a function of the process temperature elevation, an increase of graphite atoms, migrating towards the interface, and a reduction of graphite atoms at the nodular graphite diameters was noticed.
Açıklama
Anahtar Kelimeler
[No Keyword]
Kaynak
Praktische Metallographie-Practical Metallography
WoS Q Değeri
Q3
Scopus Q Değeri
Q4
Cilt
43
Sayı
6