The Effect of Welding Speed on the Laser Welding of AISI 430 Ferritic Stainless-AISI 1010 Low-Carbon Steel
[ X ]
Tarih
2009
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Carl Hanser Verlag
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
In this study, the effect of welding speed on the laser welding of AISI 430 ferritic stainless steel with AISI 1010 low-carbon steels was investigated. Laser welding experiments, were carried out under argon atmosphere, 2000 W constant welding power and 100, 200,300 cm/min welding speeds. The microstructures of the welded joints were examined by optical microscopy and SEM analysis. The tensile strength of the welded joints was measured. The result of all observations, tests and measurements indicated that the best properties were observed at the specimens welded at 100 cm/min welding speed.
Açıklama
Anahtar Kelimeler
[No Keyword]
Kaynak
Praktische Metallographie-Practical Metallography
WoS Q Değeri
Q3
Scopus Q Değeri
Q4
Cilt
46
Sayı
11