The effect of the welding temperature on the weldability in diffusion welding of martensitic (AISI 420) stainless steel, with ductile (spheroidal graphite-nodular) cast iron

Basit Öğe Kaydı
dc.contributor.authorKolukisa, Sedat
dc.date.accessioned2024-04-24T16:15:09Z
dc.date.available2024-04-24T16:15:09Z
dc.date.issued2007
dc.departmentDicle Üniversitesien_US
dc.description.abstractIn this study, the effect of welding temperature on the weldability in diffusion welding of martensitic (AISI 420), stainless steel with ductile (spheroidal graphite-nodular) cast iron was investigated experimentally under protective atmosphere at various temperatures and constant prescribed pressure blow those which would cause macrodeformation. Microstructure examinations were carried out by SEM and EDS. Hardness values were measured by Hv scale under a load of 200 g along the weld interface, mutual chrome and carbon diffusion were observed on ductile cast iron side and stainless steel side, respectively. On the other hand, as a function of process temperature elevation, increase in the amount carbon and chrome atoms migrated toward to interface, reduction at nodular graphite diameters was also noticed. As a result of all evaluations and tests carried out, it can be said that, best gathered mechanical and metallurgical properties were observed at the specimen bonded at 1100 degrees C process temperature at 12 MPa, for 20 min. (c) 2006 Elsevier B.V. All rights reserved.en_US
dc.identifier.doi10.1016/j.jmatprotec.2006.11.148
dc.identifier.endpage36en_US
dc.identifier.issn0924-0136
dc.identifier.issue1-3en_US
dc.identifier.scopus2-s2.0-33847292328
dc.identifier.scopusqualityQ1
dc.identifier.startpage33en_US
dc.identifier.urihttps://doi.org/10.1016/j.jmatprotec.2006.11.148
dc.identifier.urihttps://hdl.handle.net/11468/15676
dc.identifier.volume186en_US
dc.identifier.wosWOS:000245478600006
dc.identifier.wosqualityQ2
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.language.isoenen_US
dc.publisherElsevier Science Saen_US
dc.relation.ispartofJournal of Materials Processing Technology
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectDiffusion Welding/Bondingen_US
dc.subjectMartensitic Stainless Steelen_US
dc.subjectDuctile Cast Ironen_US
dc.titleThe effect of the welding temperature on the weldability in diffusion welding of martensitic (AISI 420) stainless steel, with ductile (spheroidal graphite-nodular) cast ironen_US
dc.titleThe effect of the welding temperature on the weldability in diffusion welding of martensitic (AISI 420) stainless steel, with ductile (spheroidal graphite-nodular) cast iron
dc.typeArticleen_US

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu