Effect of cobalt nanoparticles on mechanical properties of Sn–58Bi solder joint
Yükleniyor...
Tarih
2022
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Brittle phases are responsible for crack formation and propagation in tin–bismuth (Sn–58Bi) solder material. The purpose of this work is to investigate the effects of various cobalt (Co) nanoparticle (NP) concentrations on the tensile properties of the Sn–58Bi solder matrix. Different aging times were studied to find out the effect of Co NP on ultimate tensile strength. Tin–bismuth solder joints of different Co NP concentrations of 0%, 0.5%, 1%, and 2% were prepared. The reflow process was done at 180 °C for 1 min. Scanning Electron Microscopy and Energy-Dispersive X-ray spectroscopy were used to analyze the solder joints. The tensile test was carried out for the Sn–58Bi and Sn–58Bi–xCo (x = 0.5, 1, and 2) solder joints. The tensile test was run before and after aging time. The tensile results reveal that the addition of Co NP increased the tensile strength significantly at different concentrations of Co NP. The Tensile test revealed that ductility was improved as the temperature was increased. As the aging time increased, the ultimate tensile strength of all samples decreased.
Açıklama
Anahtar Kelimeler
Cobalt, Energy dispersive spectroscopy, Nanoparticles
Kaynak
Journal of Materials Science: Materials in Electronics
WoS Q Değeri
Q2
Scopus Q Değeri
Q2
Cilt
33
Sayı
28
Künye
Bashir M. N., Saad, H. M., Rizwan, M. Bingöl, S., Channa, I. A., Gül, M. ve diğerleri. (2022). Effect of cobalt nanoparticles on mechanical properties of Sn–58Bi solder joint. Journal of Materials Science: Materials in Electronics, 33(28), 22573-22579.