Effect of smear layer removal using different chelators on push-out bond strength of bioceramic sealer
Yükleniyor...
Tarih
2023
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Ariesdue Srl
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Aim: The aim of this study was to evaluate the effects of phytic acid (IP6), ethylenediaminetetraacetic acid (EDTA) and glycolic acid (GA) used as a final irrigation solution on the push-out bond strength (POBS) of a bioceramic-based root canal sealer. Methodology: The study included 60 single-root human mandibular premolars. After the teeth were decoronated, they were cleaned and shaped using the #25.08 Reciproc R25 single file system. Throughout preparation, each canal was irrigated using 20 ml 5.25% sodium hypochlorite (NaOCl). The teeth were divided into 4 group, each consisting of 15 (n=15) according to the final irrigation agent [1% IP6, 10% CI, 17% EDTA, and distilled water (DW)]. The final irrigation protocol consisted of application of 5 ml chelating agent for 1 minute followed by 5 ml 5.25% NaOCl application. Root canals were filled using Well Root ST canal sealer and Reciproc R25 gutta-percha, based on the single-cone technique. A 2-mm section was extracted from the middle part of the roots to test for POBS. Values were recorded in MPa and fracture types were examined. Groups were compared using one-way ANOVA (Welch’s) test. Results: The GA, EDTA, and IP6 groups showed no significant intergroup differences (p>0.05). EDTA and GA groups had significantly higher POBS than the DW group (p[removed]0.05). Conclusion: GA increased the bond strength of the bioceramic-based canal sealer to the root canal dentin at least as much as EDTA; IP6 exhibited similar strength to these chelators, it was not better than DW.
Açıklama
Anahtar Kelimeler
EDTA, Glycolic acid, Phytic acid, Push-out bond strength, Well Root ST
Kaynak
Giornale Italiano di Endodonzia
WoS Q Değeri
N/A
Scopus Q Değeri
Q4
Cilt
37
Sayı
1
Künye
Özata, M. Y., Kaya, S., Yolcu, E. N., Okumuş, T. B. ve Falakaloğlu, S. (2023). Effect of smear layer removal using different chelators on push-out bond strength of bioceramic sealer. Giornale Italiano di Endodonzia, 37(1), 46-53.